PyroCide White is a water-based latex intumescent coating specifically designed for spray application on wood based building materials. It is non-yellowing, high hiding, low gloss, and clean white in appearance.
Weight/gallon: 10.9 ± 0.2 lbs.
Viscosity: 2,500 ± 500 cps (Brookfield, #3 at 12 rpm)
Solids: 54.3% ± 1.5%
pH: 8.0 ± 0.5
PyroCide White is applied by spray, dip, roller, or brush. It imparts excellent flame retardancy to: paperboard and paperboard products, including:
Fibrous substrates coated with PyroCide White experience markedly improved flame retardancy. Specific flame retardancy ratings are available from the manufacturer.
When exposed to high temperature or flames, PyroCide White bubbles and foams into a thick, non-flammable, multi-cellular, carbonaceous char layer which insulates the fuel source (protected material) from heat while also restricting the flow of oxygen to the fuel source. The coating reacts with itself to form an insulative, foamed char barrier. This is distinctly different from salt-based flame retardants which must partially decompose the â€œprotectedâ€ material to limit flame spread.
NOTE: While PyroCide White functions extremely well on many materials, it does not provide flame retardancy to every fibrous substrate. The buyer accepts liability for determining whether the product is suitable for the buyer's intended use.
The product is available in 5-gallon pails or 55-gallon drums.
It should not be repackaged without consulting PyroTech.
PyroCide White is PERISHABLE IF FROZEN. Therefore, it MUST BE STORED IN A PROTECTED AREA AT A TEMPERATURE ABOVE 36 DEGREES FAHRENHEIT.
PyroCide White is also PERISHABLE WHEN EXPOSED TO SUSTAINED TEMPERATURES OF OVER 120 DEGREES FAHRENHEIT. Appropriate storage precautions should be taken.
Wear protective mask, gloves, and safety goggles to avoid potential nasal, throat, skin, or eye irritation while applying the product by spray. While it is non-toxic, the product may cause skin irritation in certain individuals.
Stir PyroCide White before use to re-disperse its components.
DO NOT SHAKE — foaming may result.
Clean all equipment immediately following use with warm water and mild detergent. Once dry PyroCide White I is not water soluble, resists most solvents and acids. Strong alkalis will react with the coating to give off ammonia.
Clean immediately with an absorbent if PyroCide White is spilled.
PyroCide White contains no solvents or hazardous chemical components. The following procedures, though, should be followed when using the product:
A Class A fire rating (flame spread of 25 or less - ASTM E-84) is achieved when PyroCide White is applied to Douglas fir, plywood, and oriented strand board. The application rate is two coats of PyroCide White at one gallon per 150 square feet per coat. This is approximately 8 mils per wet coat or 4 mils per dry coat.
Surface must be free of grease, dirt, rust, and loose or powdery paint. Before applying PyroCide White to a previously painted or treated substrate, users should verify that bonding compatibility exists. PyroCide White has excellent adhesive properties, but those characteristics vary with different types and thicknesses of paints, varnishes, resins, et cetera.
Recoating or topcoating of PyroCide White with any other paint or coating will change the fire ratings. If a topcoating is required, consult PyroTech for specific recommendations.
Apply by brush, roller, flat applicator or spray. Full, even coats must be applied to the mil thickness required. Conventional or air assisted airless spray equipment may be used. When using spray equipment, apply in even strokes to the specified film thickness build-up.
NOTE: coverage figures do not include spray loss.
The coating must be thoroughly mixed before using.
Thinning of the product is NOT RECOMMENDED. If thinning has to be done, use a minimum amount of water (½ pint/gallon). If thinning is done, remember it may affect the flame spread rating unless the proper dry mil thickness is built up.
Drying time depends on temperature, humidity, and degree of air movement. Generally the coating will dry to touch in 30 minutes. To recoat, it is recommended that the coating be allowed to dry for one hour.